1.Study on sintering properties of fine ore from goa india
港陆烧结配矿方案的研究
2.Preparation and sintering properties of bati4o9 by citric acid gel method
9柠檬酸凝胶法制备及烧结特性
3.Sintering properties and reaction process of - sialon alumina silica composite in coke bed at high temperatures
2系材料烧结性能及反应过程研究
4.Effects of additives on the sintering properties and electric conductivity of nife2 o4 spinel anode materials
掺杂对镍铁尖晶石阳极材料烧结性能及电导率的影响
5.The camber development mechanism and the influence factors were researched by geometry analysis , viscous analysis and sintering kinetics analysis . the camber model was established and the equation for calculating curvature of camber was proposed . the influence factors for camber involve the original size of composite , the sintering properties and the shrinkage mismatch between the two materials
从几何学、粘弹性力学和烧结动力学的不同角度出发,探讨了共烧翘曲形成机制和影响因素,建立了介电材料铁氧体材料叠层共烧翘曲模型和翘曲曲率方程,揭示影响翘曲的因素为形状尺寸因子,材料的烧结特性和异种材料之间的收缩率差,其中烧结过程的收缩率差是翘曲产生的根本因素,收缩率差越大,则翘曲曲率越大。
6.The solid reaction synthetic process , sintering properties and phase composition of the lsgm samples are investigated by tg - dta , sem , xrd and the archimedes method . the results reveal that the sintering technology generated significant influence on the sintering properties of the lsgm samples . the optimum synthesis parameters to prepare lsgm electrolyte with a pure perovskite - type structure were ascertained ; the sintering temperature and chemical constitution contributed greatly to the phase composition , the solid solubility limit of lsgm electrolyte increased with increasing of the sintering temperature , and we made lsgm electrolyte of single - perovskite structure above 1400 #
本文采用改进埋烧法制备出la _ ( 0 . 8 ) sr _ ( 0 . 2 ) ga _ ( 1 - y ) mg _ yo _ 3 ( lsgm )电解质,对制备方法与工艺参数、材料结构、电学性能以及热学性能进行了研究,分析了组成、结构与导电性能的关系,探讨了离子传输机制,其目的在于为该类离子导体的进一步研究和应用提供实验和理论依据。
7.In the process of making 95 alumina ceramics , selected five kinds of alumina powder and studied the influence of different alumina powder on the sintering properties and mechanic properties of 95 alumina ceramics , moreover , selected the most agreeable alumina powder according to the apparatus for granularity analysis and scanning electron microscope ( sem ) . the influence of different sintering temperature on the sintering mechanic properties , the microstructure of 95 alumina ceramics were investigated by adding y2o3 and la2o3 as two kinds of rare earth additives in alumina ceramics . the results indicated that the additive of la2o3 could improve the properties of 95 alumina ceramics more effectively and could get fine grain and tabular alumina that can enhance the strength of the material
选用了五种al2o3粉料,研究了其对95al2o3瓷烧结性能和力学性能的影响,并结合粒度分析仪sem对al2o3粉料进行优选;通过添加y2o3 、 la2o3两种稀土添加剂,研究了不同烧成温度对95al2o3瓷的烧结性能、力学性能及显微结构等的影响,结果表明:添加la2o3可以有效提高95氧化铝瓷烧结性能和力学性能,形成细晶和板状氧化铝瓷的显微结构;通过对比不同氧化铝粉料制备氧化铝瓷烧成温度曲线与烧结性能的关系,确定最佳的烧成温度范围为1570 ~ 1600 。
8.We found that the samples initial sintering temprature has increased from 1033 to 1216 , the sample ' s ultimate shrink ratios are 18 . 2 % and 16 . 0 % at 1600 from the heating up curves . these phenomena indicated that nanoscale m - zro2 hinders the sintering property of composites
从样品的升温曲线可以看出,加入纳米m - zro _ 2以后,样品的开始烧结温度提高了将近从1033提高到1216 ,在1600下,样品的最终收缩率分别为18 . 2和16 . 0 ,这些现象说明加入m - zro _ 2后样品的烧结困难程度大大增加。
Similar Words:
"sintering plant" Chinese translation, "sintering point" Chinese translation, "sintering practice" Chinese translation, "sintering process" Chinese translation, "sintering product" Chinese translation, "sintering quality" Chinese translation, "sintering rail" Chinese translation, "sintering range" Chinese translation, "sintering rate" Chinese translation, "sintering schedule" Chinese translation